IWG catalogue. our know-how is your success

IWG catalogue our know-how is your success IWG AUSTRIA Ing. W. Garhöfer Ges.m.b.H Tel. +43-(0)1-774 69 00 Fax. +43-(0)1-774 69 00-78 E-Mail: [email protected]
Author: Alaina Fisher
1 downloads 1 Views 3MB Size
IWG catalogue

our know-how is your success

IWG AUSTRIA Ing. W. Garhöfer Ges.m.b.H Tel. +43-(0)1-774 69 00 Fax. +43-(0)1-774 69 00-78 E-Mail: [email protected] www.iwgplating.at

SALES ABOUT NETWORK US - OUR- KNOW-HOW OUR KNOW-HOW IS YOUR IS YOUR SUCCESS SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - ABOUT US

ABOUT US IWG is a family owned and operated business since more than 50 years. IWG manufactures and services products for electroplating for about three generations and stands for continuity, high quality and flexibility. Thus, the company has extensive knowledge and significant experience in metal finishing. This is underscored by the variety of electroplating baths, process sequences, applications and quality requirements. Because of the intense activity in electroplating strong relationships with customers were built and the joint exchange enables IWG to optimize the products at the highest level. A flexible customer support service stands at the top; therefore the company is a reliable and innovative partner for the industry. IWG develops enhanced goods and products from environmentally safe chemicals and metals, and emphasizes on “Made in Austria”. Our values at a glance • premium quality • flexibility • service orientated • branch offices and distribution worldwide • long term partnership Ing. W. Garhöfer GesmbH | Bojanusgasse 15 | A-1220 Wien | Tel.: +43/1/774 69 00 | Fax: +43/1/774 69 00 78 | net: http://www.iwgplating.at | mail: [email protected]

www.iwgplating.at

1

SALES NETWORK - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - SALES NETWORK

SALES NETWORK

IWG WORLDWIDE

Due to our global service network IWG is able to satisfy customer requirements worldwide. With our international network IWG is in the position to serve clients flexible and regionally. We are on site during the implementation of new processes and support to set up the process parameters properly. IWG Austria – with its headquarter in Vienna – focuses on the research of new processes and the enhancement of existing products and serves as well European clients. Branch offices within the international network, particularly in the Arab and Asian regions, guarantee regional and flexible customer service. IWG Technology handles the huge Chinese market, IWG Thailand serves customers in Thailand and IWG Vietnam supports customers in Vietnam. Because of the permanent process of growing IWG broke into new markets – as Dubai, Iran, Syria, India, Ukraine, Russia and Turkey – within the last years.

IWG AUSTRIA Ing. W. Garhöfer Ges.m.b.H Tel. +43-(0)1-774 69 00 Fax. +43-(0)1-774 69 00-78 E-Mail: [email protected] www.iwgplating.at

IWG HONG KONG Technology LTD. Tel. ++852-(0)-24 246 988 Fax. ++852-(0)-24 239 733 [email protected] www.iwg-plating.com.hk

IWG THAILAND CO. LTD. Tel. ++662-(0)-921 58 85-7 Fax. ++662-(0)-921 58 84 [email protected] www.iwgplating.at

IWG TURKEY Ayba Celik Ic Ve Dis Ticaret Tel. ++90-212-603 19 73 Fax. ++90-212-603 19 74 [email protected] www.aybacelik.com

IWG UKRAINE Ayba Celik Ic Ve Dis Ticaret Tel. ++380 67 999 7694 [email protected] www.aybacelik.com

IWG RUSSIA Ayba Celik Ic Ve Dis Ticaret Tel. ++7 915 903 4952 [email protected] www.aybacelik.com

IWG IRAN Sama Chimie Saz Trading Co Tel. ++98-21-885 18 553-4 Fax. ++98-21-885 29 858 [email protected] www.samachimie.com

IWG UNITED ARAB EMIRATES Sama Chimie Saz International Trading Tel. ++971-6-5576052 & 04 266 1208 Fax. ++971-6-5576053 & 04 266 1408 [email protected]

IWG LEBANON Jaghlasian Trading Tel: ++961-1-48 75 18-9 Fax: ++961-1-48 75 71 www.jaghlasian.com

IWG SYRIA Jaghlasian Trading Tel. ++963-21-444 42 13-46 59 616 Fax. ++963-21-446 44 70 [email protected] www.jaghlasian.com

IWG IRAN IWG LEBANON

IWG TURKEY

IWG INDIA MUMBAI IWG UKRAINE IWG SYRIA

IWG INDIA MUMBAI M. Sakshi international Tel: ++91-22-2341 01 79 Fax: ++91-22-40 05 16 77 [email protected]

IWG INDIA JAIPUR Arihant Sai Traders Tel: ++91-141-27 92 261 Fax: ++91-141-27 92 280

www.iwgplating.at

IWG THAILAND

IWG RUSSIA IWG INDIA JAIPUR

IWG AUSTRIA

IWG HONG KONG

IWG UNITED ARAB EMIRATES

3

SERVICE - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - CUSTOMERS

SERVICE

CUSTOMERS

“Our know how is your success”

Atotech Österreich, Hans Andersen GmbH, Arts Group, AT&S AG, Atotech Österreich GmbH, CERATIZIT Austria GmbH, CEST - Kompetenzzentrum für elektrochemische Oberflächentechnologie GmbH, Colibra, Collini Wien GmbH, Crystalline Co. LTD, Dr. Ofner GmbH, Electrovac Hacht & Huber GmbH, Electrovac Metall-Glaseinschmelzungs GmbH, Galvalux s.r.l., Gee Lee Metal And Plastic Mfy. Ltd., Henkel & Grosse GmbH & Co KG, Honour Code Industrial Ltd., HTM Sport GmbH, IMA Engineering Services Limited, Infineon Technologies Austria AG, Italina (Holdings) Limited, Johnson Gems And Jewellery Manufactory Limited, Killine Optical Ltd., Konplott s.a.r.l., Kudrna GesmbH, Lenhard GmbH, Logo SA, Luvata Austria GmbH, Luxottica, m.p. group, Marigot Jewellery, MEC Europe NV, Menrad Schweiz AG, Miba Gleitlager GmbH, Münze Österreich AG, Neva Limited, Ögussa GmbH, Otto Dunkel GmbH, Pac Tech GmbH, Panasonic Electric Works Austria GmbH, Plansee SE, P.T. Luxindo Nusantara, Ralf Thome, Rathenower Optik GmbH, RSF Elektronik GmbH, Schmidt Technology GmbH, Schott Electronic Packaging GmbH, SG-Galvanobedarf GmbH, Silhouette International Schmied AG, S-K-M electronics GmbH, Sony DADC Austria AG, Stork Prints Austria GmbH, Sun Hing Optical Manufactory Ltd., Swarovski AG, Technische Universität Graz, Technische Universität Wien, TYCO Electronics Austria GmbH, Tyrolit Schleifmittelwerke Swarovski K.G., Umicore Galvanotechnik GmbH, W & H Dentalwerk Bürmoos GmbH, Wah Ming Optical Manufactory Ltd., Wallpach Arno Metallwarenfabrik GmbH, Wild GmbH, Win-Chance Metal Factory Ltd., ...

With our excellent research and development facilities combined with decades of experience and a broad range of surface finishing products and processes we are a reliable partner for the electroplating industry with customer proximity as our top priority. Attentive to customers´ needs we have successfully developed, introduced and attended a series of procedures. We provide standard plating sequences as well as customer-tailored solutions to plate different base materials as well as several finishes. We are continuously monitoring and improving our products to make sure that we provide our customers always the best possible solution. Special attention and focus is given to the close connection with our customers while implementing the process. This service includes consultations, make up of bathes and production of representative pre-series together with our technicians as well as control of the electrolytes and various tests of the plated products.

and many more ...

www.iwgplating.at

5

OVERVIEW - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - OVERVIEW

OVERVIEW PRETREATMENT ELECTROLESS PLATING ELECTROLYTIC PLATING - Rhodium - Palladium - Ruthenium - Platinum - Gold - Silver - Bronze - Copper PEN PLATING POSTTREATMENT RECOVERY EQUIPMENT QUALITY ASSURENCE AND LAB

www.iwgplating.at

7

PRETREATMENT - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PRETREATMENT

PRETREATMENT

DEGREASING

When cleaning surfaces the versatility of ultrasonic degreasing is getting visible. Highest grades of cleaning can be reached in comparatively short times. Advantages can be seen especially when cleaning geometric complex items. Ultrasonic is also effective on unapproachable areas where mechanical and manual cleaning like spraying and brushing fails. IWG Ultrasonic cleaners dissolve and suspend impurities, inhibit metal surfaces and saponify oils and greases.

Degreasing 1018

US Cleaner The ultrasonic cleaner US Cleaner is a solid mixture of surfactants and salts especially developed for cleaning nonferrous and precious metals in the ultrasonic cleaning process. The cleaner can be used especially for removing polishing pastes. Process Conditions: Working temperature: Rate of application:

20-75°C 20 g/l

Uniclean 70 The ultrasonic cleaner Uniclean 70 is a weak alkaline cleaner, a mixture of different surfactants and organic additives. Uniclean 70 was developed especially for removing polishing pastes and produces a temporary corrosion protection after cleaning. Process Conditions: Working temperature: Rate of application:

www.iwgplating.at

The silicate and cyanide free salt mixture Degreasing 1018 is designed for electrolytic degreasing and activation of iron, copper, brass, white die-castings and zinc based die-castings. The product contains chelating agents, which dissolve oxides - that makes the ready degreasing solution insensible against hardness components of the water. Instead of silicates other builders are used to reach a high dispersing ability. Process Conditions: Working temperature: 20-60°C Current density: 5-10 A/dm² Time of exposition: 0,5-4 min.

Degreasing 1018 M The silicate and cyanide free salt mixture Degreasing 1018 M is designed for the electrolytic degreasing and activation of iron, copper, brass, white die-castings and zinc based die-castings. The product contains chelating agents, which dissolve oxides - that makes the ready degreasing solution insensible against hardness components of the water. Instead of silicates other builders are used to reach a high dispersing ability. Degreasing 1018 M is low foaming. Process Conditions: Working temperature: 20-60°C Current density: 5-10 A/dm² Time of exposition: 0,5-4 min.

40-60°C 20-50 g/l

9

PRETREATMENT - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - ELECTROLESS PLATING

ELECTROLESS PLATING Degreasing 1070 The cyanide free high alkaline salt mixture Degreasing 1070 is designed for the electrolytic degreasing and activation of iron and copper alloys. The product contains chelating agents, which dissolve oxides - that makes the ready degreasing solution insensible against hardness components of the water. Process Conditions: Working temperature: for copper alloys: 20-60°C for stainless steel: 20-50°C Current density: for copper alloys: 1-4 A/dm² for stainless steel: 4-6 A/dm²

Sudinor The electroless goldbath Sudinor deposits without current simply by ionexchange on less precious metals especially on nickel, copper and their alloys, gold with constant colour over a wide range of gold contents. The process is mainly used for printed circuits on electroless nickel to prevent oxidation and substitute for HAL. Process Conditions: Working Temperature: 70-100°C, higher temperatures increase deposition rate pH-value: iron, electroless nickel 4,0-4,5 copper alloys 4,0

Deposit characteristics: pure gold - 24 ct

Degreasing 1013 The silicate and cyanide free salt mixture Degreasing 1013 is designed for the electrolytic degreasing and activation of iron, copper and brass. The product contains chelating agents, which dissolute oxides and makes the ready degreasing insensible against water hardness. Instead of silicates other builders are used to reach the high dirt dispersing ability. The product Degreasing 1013 is a dry mixture of salt with practical unlimited shelf life. Process Conditions: Working temperature: 20-60°C Current density: 5-10 A/dm² Time of exposition: 0,5-4 min.

www.iwgplating.at

11

ELECTROLESS PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - ELECTROLESS PLATING

Nickless HMF

Nickless Mid Phos

Nickless HMF is a highly stable, ammonia-free, electroless nickel plating bath. The stabilizer system is free of heavy metals. Nickless HMF is designed to produce a corrosion resistant, high phosphorus deposit free of lead on steel, iron, stainless steel, aluminium, copper alloys and nickel alloys, berylium, titanium and other substrates. The self adjusting pH feature both simplifies operation and makes the bath ideal for use with automatic controllers. Nickless HMF produces a pore-free, semi-bright, non staining deposit on properly prepared substrates. Advantages: • High corrosion resistant deposit (passes nitric acid test) • Non-ammoniated system • Ductile, pore free, semi-bright deposit • High phosphorus content • Suitable for a wide range of substrates • Consistent rate • Extended bath life on aluminium • Nonmagnetic deposit • Stabilizer system free of heavy metals • Excellent bath stability • Self adjusting pH

Nickless Mid Phos is a stable, ammonia-free, electroless nickel plating bath. Nickless Mid Phos is designed to produce a corrosion resistant deposit on steel, iron, stainless steel, aluminium, copper alloys and nickel alloys, beryllium, titanium and other substrates. The self adjusting pH feature both simplifies operation and makes the bath ideal for use with automatic controllers.

Process Conditions: Nickel content: 6,1 g/l pH - value: 4,8-5,1 Rate of deposit: 13 µ/h at 88°C

www.iwgplating.at

Deposit characteristics: Nickel content: 87-88 % Phosphorus content: 11-13 % Density: 7,9 g/cm³ Magnetics: as plated nonmagnetic heat treated 1 hour at 275°C nonmagnetic Hardness (kg/mm²): as plated 525 HK100 heat treated 1 hour at 400°C 810 HK100

Nickless Mid Phos produces a pore-free, semi-bright, non staining deposit on properly prepared substrates. Advantages: • Non-ammoniated system • Middle phosphorus content • Ductile, pore free, • Consistent rate • Semi-bright deposit • Excellent bath stability • Suitable for a wide range of substrates • Self adjusting pH Process Conditions: Nickel content: 6,1 g/l pH - value: 4,8-5,1 Rate of deposit: 20 µ/h at 88°C

Deposit characteristics: Nickel content: 91-95 % Phosphorus content: 5-9 % Density: 8,1 g/cm³ Magnetics: as plated magnetic Hardness (kg/mm²): as plated 550 HK100

13

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

PLATING Rhodium blue

RHODIUM Rhodium white C2 The pure rhodium process Rhodium white C2 is an acidic electrolyte, from which brilliant white layers can be deposited. Application: real jewellery, custom jewellery, optical frames, watches. Process Conditions: Working temperature: Current density: Rhodium content: Rate of deposit:

20-50°C 1-5 A/dm² 2,0 g/l 0,1µ in 1 min. at 1A/dm²

Deposit characteristics: Colour: white

The pure rhodium process Rhodium blue is an acidic electrolyte from which blue layers can be deposited. Application: real jewellery, custom jewellery, optical frames, watches. Process Conditions: Working temperature: Current density: Rhodium content:

35°C 1 A/dm² 2,0 g/l

Deposit characteristics: Colour: blue

Rhodalloy Rhodium black The pure rhodium process Rhodium black is an acidic electrolyte, from which black abrasion- and corrosion-resistant layers can be deposited. Application: real jewellery, custom jewellery, optical frames, watches. Process Conditions: Working temperature: Current density: Rhodium content: Rate of deposit:

30°C 1-3 A/dm² 2,0 g/l 0,1µ in 1 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Colour: black

The rhodium-ruthenium process Rhodalloy is an acidic electrolyte from which brilliant white layers with an appearance close to pure Rhodium can be deposited. The rhodium-ruthenium layers contain 70-80 % Rhodium and 30-20 % Ruthenium depending on the bath composition. Application: real jewellery, custom jewellery, optical frames, watches, electric contacts. Process Conditions: Working temperature: Current density: Rhodium content: Rate of deposit:

45°C 1-5 A/dm² 1,6 g/l 0,1µ in 2 min. at 1A/dm²

Deposit characteristics: Alloying component: Ru Colour: white

15

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

PALLADIUM Palladium Gapal FS

Palladium Gapal TS

The pure palladium process Gapal FS is a weak alkaline electrolyte, from which bright decorative white pure palladium layers can be deposited. Layers of Gapal FS can be used up to about 0,5 microns as a diffusion barrier or as flash palladium in the bijou and optical frame production.

The pure palladium process Gapal TS is a weak alkaline electrolyte, from which bright, decorative white levelled pure palladium layers can be deposited. Gapal TS has been formulated to get crack free and non porous layers. Gapal TS enables deposits of thicknesses above 5 microns with mirror bright finish that is the reason why it is used as an excellent corrosion protection nickel substitute. Application: watch, bijou and optical frame production.

Process Conditions: Working temperature: Current density: Palladium content: Rate of deposit:

25-30°C 0,5-1 A/dm² 2,0 g/l 0,1µ in 1 min. at 0,5A/dm²

Deposit characteristics: Colour: white

Process Conditions: Working temperature: pH-value: Current density: Palladium content: Rate of deposit:

20-30°C 9,0 0,5-1 A/dm² 10,0 g/l 1µ in 4 min. at 1A/dm²

Deposit characteristics: Colour: white

Palladium Gapal HT The pure palladium process Gapal HT is a weak alkaline electrolyte, from which bright, decorative white levelled pure palladium layers can be deposited. Gapal HT has been formulated to get crack free and non porous layers. Gapal HT enables deposits of thicknesses above 5 microns with mirror bright finish that is the reason why it is used as an excellent corrosion protection nickel substitute. Application: watch, bijou and optical frame production. Process Conditions: Working temperature: pH-value: Current density: Palladium content: Rate of deposit:

40-45°C 7,2-8,2 0,5-1 A/dm² 10,0 g/l 1µ in 4 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Colour: white

Palladium 174 C2 The palladium nickel process 174 C2 is an ammonia based electrolyte from which a bright palladium-nickel alloy with a composition of about 80 % palladium and about 20 % nickel can be deposited. Application: watch, bijou and optical frame production. Process Conditions: Working temperature: pH-value: Current density: Palladium content: Rate of deposit:

35°C 7,5 0,5-1 A/dm² 8,0 g/l 1µ in 3 min. at 1A/dm²

Deposit characteristics: Alloying component: Ni Colour: white

17

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

PLATINUM Palladium Gapal Co

Platinumbath

The Gapal Co process is an ammonia based electrolyte from which a bright palladium-cobalt alloy with a composition of about 80 % palladium and about 20 % cobalt can be deposited. The process is suitable for rack and barrel application. The Gapal Co process may be used as a substitute to Pd/Ni for barrier plating to prevent copper migration into gold top coat. Gapal Co deposits have excellent corrosion protection properties. Application: watch, bijou and optical frame production.

The Platinumbath is a strong acidic electrolyte, which has especially been developed to deposit very hard, bright platinum layers of high purity. The bath is easy to control with excellent throwing power, the layers are free of pores with extraordinary abrasion and tarnish resistance. The deposits are nearly as white as rhodium deposits. Therefore layers produced by Platinum can be used as a substitute for Rhodium. Application: real jewellery, custom jewellery, optical frames, watches.

Process Conditions: Working temperature: pH-value: Current density: Palladium content: Rate of deposit:

24-37°C 8,2 0,5-1 A/dm² 4,0 g/l 1µ in 5 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Alloying component: Co Colour: white

Process Conditions: Working temperature: Current density: Platinum content: Rate of deposit:

40-60°C 0,5-1,5 A/dm² 2,5-3 g/l 0,1µ in 1,5 min. at 1A/dm²

Deposit characteristics: Colour: white

19

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

RUTHENIUM Ruthenium Rugadec HS2

Ruthenium Rugadec N

The ruthenium process Rugadec HS2 is an acidic plating electrolyte, which produces bright ruthenium deposits. The electrolyte is easy to control and deposits hard layers free of pores of extraordinary abrasion resistance and good throwing power. The colour scale ranges from light grey over middle grey to anthracite and can be adjusted depending on the amount of replenisher added. The electrolyte can be used for technical and decorative applications. Especially when applied to bicolourproducts the effect of gold layers partly covered by ruthenium is amazing.

The ruthenium Rugadec N process is a neutral plating electrolyte which produces dark bright ruthenium deposits. Rugadec N is mainly used for the deposition of decorative layers for watches, jewellery as well as for the spectacle frame industry. Process Conditions: Deposit characteristics: Working temperature: 60-65°C Colour: dark grey Current density: 1-2 A/dm² Ruthenium content: 2-4 g/l Rate of deposit: 0,1µ in 2 min. at 1A/dm²

Process Conditions: Working temperature: Current density: Ruthenium content: Rate of deposit:

60°C 1-2 A/dm² 2-5 g/l 0,1µ in 3 min. at 1A/dm²

Deposit characteristics: Colour: light grey- anthracite

Ruthenium Rugadec HS2/O The ruthenium process Rugadec HS2/0 is an acidic plating electrolyte, which produces bright ruthenium deposits. The electrolyte is easy to control and produces hard layers free of pores of extraordinary abrasion resistance and good throwing power. The deposits have a dark grey colour with an L*-value of 50. The electrolyte can be used for technical and decorative applications. Especially when applied to bicolour-products the effect of gold layers partly covered by ruthenium is amazing. Process Conditions: Working temperature: Current density: Ruthenium content: Rate of deposit:

60°C 1-2 A/dm² 2-5 g/l 0,1µ in 4 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Colour: dark grey

21

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

GOLD STRIKES

COLOURGOLD

Gold MC 210 H

Gold Auroprint

This electrolyte is designed for strike gold deposition on stainless steel and on nickel alloys. The deposit is smooth, yellow and bright. This process is suitable for rack and barrel plating.

The colour gold process Auroprint is a weak acidic electrolyte, from which bright colour constant layers with a hardness of 140 - 160 HV can be deposited. The electrolyte works over a wide range of gold contents. This type of bath is mainly used in the custom jewellery or electronic industry.

Process Conditions: Working temperature: Current density: Gold content:

20-25°C 0,5-2 A/dm² 1-1,5 g/l

Gold MC 211 Ti This electrolyte is designed for strike gold deposition on titanium and stainless steel. The deposit is smooth, yellow and bright. This process is suitable for rack and barrel plating. Process Conditions: Working temperature: Current density: Gold content:

20-25°C 0,5-2 A/dm² 1-1,5 g/l

www.iwgplating.at

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

25°C 3,7 0,5-1 A/dm² 1-8 g/l 1µ in 8 min. at 1A/dm²

Deposit characteristics: Alloying component: Co Hardness: 150 Hv Colour: 3 N

Gold MC 2N18 The colour gold process MC 2N18 is a weak acidic electrolyte, from which bright layers with constant colours and a hardness of about 200 - 240 HV can be deposited. A typical field of application is the watch, bijou and optical frame production. The gold concentration in the deposit is approx. 23 carat, the colour is about 2N. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

32°C 3,7 1 A/dm² 4 g/l 1µ in 6 min. at 1A/dm²

Deposit characteristics: Alloying component: Ni, In Carats: 23 ct Hardness: 220 Hv Colour: 2 N

23

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

Gold MC 1N14

Gold Auroprint DE

The Colourgoldprocess MC 1N14 is a weak acidic electrolyte from which bright layers with a constant pale yellow colour can be deposited. Application: watch, jewellery and optical frame production.

The colour gold process Auroprint DE is a weak acidic electrolyte, from which bright colour constant deposits can be deposited. Application: custom jewellery as well as electronic industry

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

55°C 3,6 1 A/dm² 1 g/l 1µ in 6 min. at 1A/dm²

Deposit characteristics: Alloying component: Ni, In Hardness: 220 Hv Colour: 1 N

35°C 3,7 1 A/dm² 4-6 g/l 1µ in 6 min. at 1A/dm²

Deposit characteristics: Alloying component: Co Carats: 23,5 ct Hardness: 190 Hv Colour: 3 N

Gold Auroprint 218 M

Gold MC 218 The colour gold process MC 218 is a weak acidic electrolyte, from which bright colour constant layers with a hardness of 220 - 230 HV can be deposited. This type of bath is mainly used in the custom jewellery and watchcase industry. Deposits of MC 218 are about 23 carat. Because of the absence of nickel and cobalt as allying components, MC 218 cannot cause any kind of skin allergy. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

35°C 4,0 1 A/dm² 2,5 g/l 1µ in 8 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Alloying component: Fe, In Carats: 23 ct Hardness: 220 Hv Colour: 2 N

The colourgold process Auroprint 218 M is a weak acidic electrolyte from which bright colour constant deposits can be deposited. Thicker deposites can be reached in short time. Application: custom jewellery and watchcase industry. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

35-40°C 4,2 1-2 A/dm² 8 g/l 1µ in 3 min. at 1A/dm²

Deposit characteristics: Alloying component: Co Carats: 23,7 ct Hardness: 190 Hv Colour: 3 N

25

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

GOLDBATHES FOR DEPOSITING THICK LAYERS Gold MC 1114 S

Gold MC 210 GR

The colourgold MC 1114 S process is an acidic electrolyte from which bright colourconstant pale yellow layers can be deposited. Because of the absence of nickel layers of MC 1114 S cannot cause nickel allergy on the skin. Application: custom jewellery and watchcase industry.

The pure gold bath MC 210 GR is a neutral electrolyte, from which bright layers with a thickness up to some microns can be deposited. If the base material is adequate, deposits are free of pores after some tenth parts of a micron. Layers deposited from MC 210 GR are excellent for sandwich-plating. The bath is suitable for rack plating as well as barrel plating.

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

40-50°C 2,0 0,5-1,5 A/dm² 1 g/l 1µ in 20 min. at 1A/dm²

Deposit characteristics: Alloying component: Co, In Carats: 23 ct Hardness: 230 Hv Colour: 1 N

65°C 7,0 0,2-0,5 A/dm² 4-5 g/l 1µ in 4 min. at 0,4A/dm²

Deposit characteristics: Carats: 24 ct Hardness: 80 Hv Colour: yellow

Gold MC 2001

Gold MC 1114 M The colourgold MC 1114 M process is an acidic electrolyte from which bright colourconstant very pale yellow layers can be deposited. Because of the absence of nickel layers of MC 1114 M cannot cause nickel allergy on the skin. Application: custom jewellery and watchcase industry. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

40-50°C 2,0 0,5-1,5 A/dm² 1 g/l 1µ in 20 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Alloying component: Co, In Carats: 23 ct Hardness: 230 Hv Colour: 1 N

The colour gold process MC 2001 is a weak alkaline sulphite electrolyte, which produces mirror bright, ductile, levelled, pink coloured deposits. Application: decorative plating in the jewellery as well as optical frame industry. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

55°C 9,5 0,2-0,8 A/dm² 8 g/l 1µ in 3 min. at 1A/dm²

Deposit characteristics: Alloying component: Pd, Cu Carats: 22 ct Hardness: 290 Hv

27

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

Gold MC 9000

Gold MC 9020

The colour gold process MC 9000 is a neutral sulphite electrolyte, which produces mirror bright deposits. Layers which are deposited by MC 9000 are extraordinary corrosion resistant and colour constant up to 250°C Application: decorative plating in the spectacle frame industry as well as for watches and jewellery

The colour gold process MC 9020 is a neutral sulphite electrolyte which produces ductile pale, slightly pink coloured deposits. Application: decorative plating in the spectacle frame industry as well as for watches and jewellery.

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

55°C 7,0 0,3-0,8 A/dm² 3-5 g/l 1µ in 2,7 min. at 0,7A/dm²

Deposit characteristics: Alloying component: Pd Carats: 21-22 ct Hardness: 290 Hv Colour: pale-yellow

55°C 7,0 0,2-0,7 A/dm² 1 g/l 1µ in 20 min. at 0,5A/dm²

Deposit characteristics: Alloying component: Pd Hardness: 290 Hv Colour: rosé

Gold MC 118 GD

Gold MC 9005 The colour gold process MC 9005 is a neutral sulphite electrolyte which produces ductile rosé coloured deposits. Application: decorative plating in the spectacle frame industry as well as for watches and jewellery. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

55°C 7,0 0,2-0,7 A/dm² 4 g/l 1µ in 3,8 min. at 0,5A/dm²

www.iwgplating.at

Deposit characteristics: Alloying component: Pd,Cu Carats: 21 ct Hardness: 290 Hv Colour: rosé

The hard gold process MC 118 GD is a cyanide electrolyte from which ternary alloys of gold, copper, cadmium can be deposited. MC 118 GD layers are up to 40 microns mirror bright. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

70°C 9,7 1 A/dm² 6 g/l 1µ in 2,5 min. at 1A/dm²

Deposit characteristics: Alloying component: Cu, Cd Carats: 18 ct Hardness: 400 Hv Colour: 2N

29

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

Gold MC 118 PI

Gold MC 3010 Argor

The gold process MC 118 PI is a cyanide electrolyte from which alloys of gold and copper can be deposited. The deposited layer has about 16 - 18 carats. This type of process is used for decorative plating in the jewellery as well as optical frame industries. The deposits are bright, ductile and slightly levelling.

The gold-silver-bath MC 3010 Argor is a cyanidic, alkaline electrolyte which produces mirrorbright, pale-yellow deposits of 10 carats. Application: decorative plating in the jewellery as well as optical frame industry.

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

65°C 9,7 0,4-1,5 A/dm² 5 g/l 1µ in 3,3 min. at 1A/dm²

Deposit characteristics: Alloying component: Cu Carats: 16-18 ct Colour: pink

45°C 11,0 1,5 A/dm² 4 g/l 1µ in 1,5 min. at 1,5A/dm²

Deposit characteristics: Alloying component: Ag Carats: 10 ct Hardness: 220 Hv Colour: pale-yellow

Gold MC 3020 Argor

Gold MC 3000 Argor The gold-silver-bath MC 3010 Argor is a cyanidic, alkaline electrolyte which produces mirrorbright, pale-yellow deposits of about 220 Hv and 13,5 carats. Application: decorative plating in the jewellery as well as optical frame industry. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

45°C 10,4 1,5 A/dm² 6 g/l 1µ in 1,1 min. at 1,5A/dm²

www.iwgplating.at

Deposit characteristics: Alloying component: Ag Carats: 13,5 ct Hardness: 220 Hv Colour: pale-yellow

The gold-silver-bath MC 3020 Argor is a cyanidic, alkaline electrolyte which produces mirrorbright, deposits of 20 carats. Application: decorative plating in the jewellery as well as optical frame industry. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

25°C 11,0 0,5 A/dm² 8 g/l 1µ in 2,4 min. at 0,5A/dm²

Deposit characteristics: Alloying component: Ag Carats: 20 ct Hardness: 140 Hv Colour: lemon-yellow

31

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

Gold MC 3030 Argor The gold-silver-bath MC 3030 Argor is a cyanidic, alkaline electrolyte which produces mirrorbright, yellowish white deposits. Application: decorative plating in the jewellery as well as optical frame industry. Process Conditions: Working temperature: pH-value: Current density: Gold content: Rate of deposit:

35°C 11,0 1,5 A/dm² 2 g/l 1µ in 1,6 min. at 1,5A/dm²

www.iwgplating.at

Deposit characteristics: Alloying component: Ag Carats: 5 ct Hardness: 220 Hv Colour: yellowish-white

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

BRIGHT SILVER PROCESS Silver Arga 380 The bright silver bath Arga 380 imparts an extraordinary white fine-silver deposit with excellent throwing power. The layers are ductile, bright, free of stress and cracks, and do not contain any metals as hardening agents. The electrolyte is well suited for decorative and technical plating tasks. Process Conditions: Working temperature: pH-value: Current density: Silver content: Rate of deposit:

20-30°C >12 0,1-3 A/dm² 35 g/l 1µ in 2 min. at 1A/dm²

Deposit characteristics: Colour: white Hardness: 120 Hv

33

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

BRONZE PROCESSES Whitebronze CT 15 LF

Yellowbronze CT 40 LF

The Whitebronzebath CT 15 LF is an alkaline cyanidic electrolyte for producing a white coloured alloy of copper, zinc and tin and is free of any toxic metals, especially free of lead. The bath can produce mirrorbright layers up to 5µ. Whitebronze CT 15 LF can be used for decorative plating in jewellery industry for nickel free products as well as on the technical sector for example for electrical contacts.

The Yellowbronzebath CT 40 LF is an alkaline cyanidic electrolyte for producing a yellow coloured alloy of copper and tin and is free of any toxic metals, especially free of lead. The bath can produce mirrorbright layers up to 5µ. Yellowbronze CT 40 LF can be used for decorative plating in jewellery industry, especially for nickel free products.

Process Conditions: Working temperature: Current density: Rate of deposit:

55°C 0,5-1,5 A/dm² 1µ in 5 min. at 1A/dm²

Deposit characteristics: Colour: white

Process Conditions: Working temperature: Current density: Rate of deposit:

45°C 0,5-1,5 A/dm² 1µ in 2 min. at 1A/dm²

Deposit characteristics: Colour: yellow

Whitebronze CT 16 LF The Whitebronzebath CT 16 LF is an alkaline cyanidic electrolyte for producing a white coloured alloy of copper and tin and is free of any toxic metals, especially free of lead. The bath can produce mirrorbright layers up to 5µ with extraordinary good corrosion resistance. Whitebronze CT 16 LF can be used for decorative plating in jewellery industry for nickel free products as well as on the technical sector for example for electrical contacts. Process Conditions: Working temperature: Current density: Rate of deposit:

55°C 0,5-1,5 A/dm² 1µ in 5 min. at 1A/dm²

www.iwgplating.at

Deposit characteristics: Colour: white

35

ELECTROLYTIC PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PLATING ELECTROLYTIC

COPPER PROCESSES IWG Cu 900 IWG Cu 900 is a high acidic copper plating bath for ABS plating with an excellent throwing power. The layer has a high durability in thermal shock test with a very good solderabilty. Process Conditions: Working temperature: Current density: Copper content: Rate of deposit:

25°C 1-3A/dm² 35 g/l 1µ in 1,7 min. at 1A/dm²

IWG Cu 550 IWG Cu 550 is an acid copper process with high levelling properties. IWG Cu 550 layers are ductile and stress free and can be plated on various substrates. Process Conditions: Working temperature: Current density: Copper content: Rate of deposit:

18-35°C 1-6 A/dm² 55 g/l 1µ in 1,5 min. at 1A/dm²

www.iwgplating.at

37

PEN PLATING - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - PEN PLATING

PEN PLATING Gold yellow 0N for pen plating Process Conditions: Description: Gold content: Colour: Working temperature: Voltage

Cyanidic 5g/l 0N 25°C 10-15V

Gold yellow 1N for pen plating Process Conditions: Description: Gold content: Colour: Working temperature: Voltage

Acidic 10g/l 1N 25°C 5-20V

Gold yellow 2N for pen plating Process Conditions: Description: Gold content: Colour: Working temperature: Voltage

Acidic 20g/l 2N 25°C 5-15V

www.iwgplating.at

Gold yellow for pen plating Process Conditions: Description: Gold content: Colour: Working temperature: Voltage

Weak acidic 10g/l 2N 25°C 5-15V

Gold Rosé 1 for pen plating Process Conditions: Description: Gold content: Colour: Working temperature: Voltage

Cyanidic 1,6g/l 4N 25°C 5-20V

Gold 5N red for pen plating Process Conditions: Description: Gold content: Colour: Working temperature: Voltage

Cyanidic 1,6g/l 5N 25°C 5-10V

39

PEN PLATING - OUR KNOW-HOW IS YOUR SUCCESS

Rhodium white 5B for pen plating Process Conditions: Description: Rhodium content: Colour: Working temperature: Voltage

Acidic 20g/l white 25°C 13V

Rhodium white 5E for pen plating Process Conditions: Description: Rhodium content: Colour: Working temperature: Voltage

Acidic 20g/l white 25°C 13V

Rhodium white 5F for pen plating Process Conditions: Description: Rhodium content: Colour: Working temperature: Voltage

Acidic 20g/l white 25°C 13V

www.iwgplating.at

OUR KNOW-HOW IS YOUR SUCCESS - PEN PLATING

Rhodium white 5G for pen plating Process Conditions: Description: Rhodium content: Colour: Working temperature: Voltage

Acidic 20g/l white 25°C 10-15V

Rhodium black 3 for pen plating Process Conditions: Description: Rhodium content: Colour: Working temperature: Voltage

Acidic 20g/l black 25°C 10-20V

Rhodium blue for pen plating Process Conditions: Description: Rhodium content: Colour: Working temperature: Voltage

Acidic 20g/l blue 25°C 10-20V

41

PEN PLATING - OUR KNOW-HOW IS YOUR SUCCESS

Palladium white for pen plating Process Conditions: Description: Palladium content: Colour: Working temperature: Voltage

Alkaline 50g/l white 25°C 10-15V

OUR KNOW-HOW IS YOUR SUCCESS - PEN PLATING

Silver white for pen plating Process Conditions: Description: Silver content: Colour: Working temperature: Voltage

Cyanidic 30g/l white 25°C 5-10V

Ruthenium natural for pen plating Process Conditions: Description: Ruthenium content: Colour: Working temperature: Voltage

Acidic 20g/l light grey 25°C 10-20V

Ruthenium black for pen plating Process Conditions: Description: Ruthenium content: Colour: Working temperature: Voltage

Acidic 20g/l black 25°C 10-20V

www.iwgplating.at

43

POSTTREATMENT - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - POSTTREATMENT

POSTTREATMENT Silverpassivation XP 0015

Antitarnish

The Silverpassivation XP 0015 on silver, is an electroless passivation bath, which deposits transparent, colourless protective coatings. The produced layer protects the silver surface from formation of silver sulphide, so decolouration can be prevented for a longer period of time. Through passivation the conductivity and soldering are only insignificant reduced.

Antitarnish has been developed to protect copper and copper alloys as well as copper coatings against corrosion. By a simple efficient immersion process a colourless, thin and adherent protective coating is achieved that provides protection against oxidation of the materials surface. Once treated the material may be stored for several months without tarnishing. Antitarnish is an aqueous, environmentally sustainable solution without the additions of chromates. Components once treated with Antitarnish can be processed further (electrochemically) after the protective coating is removed by acid dipping.

Process Conditions: Rate of application: 5-30% Working temperature: 35-50°C pH-value: 4-8,5 Time of exposition: 5-10 min.

Process Conditions: Rate of application: Working temperature: Time of exposition:

100% 20-90°C 0,1-1 min.

Silverpassivation XP 0020 Paste The Silverpassivation XP 0020 on silver, is an electroless passivation bath, which deposits transparent, colourless protective coatings. The produced layer protects the silver surface from formation of silver sulphide, so decolouration can be prevented for a longer period of time. Through the passivation the conductivity and soldering are only insignificant reduced. Process Conditions: Rate of application: 1-6% Working temperature: 35-50°C pH-value: 4-8,5 Time of exposition: 5-10 min.

www.iwgplating.at

Garcoat CA This cathodic clearcoat based on acrylic-resin is especially developed to coat decorative surfaces and can be applied between 5 µm and 35 µ. This cathodic clearcoat is an excellent protection for high-gloss metals and metallic surfaces of gold, silver, copper, chromium, nickel, aluminium, stainless steel and other alloys from atmospheric influences, as well as from everyday wear and tear. Process Conditions: Working temperature: 25-30°C pH-value: 4,8±0,3 Time of exposition: 30-180 sec. Voltage: 30-80 V(DC) Thickness of deposit: 5-35µ Tempering time: 15-25 min at 150-160°C

45

POSTTREATMENT - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - RECOVERY

RECOVERY Dyes There are several opportunities to design lacquered surfaces: • Dye the surface of the lacquer A part is first lacquered with Garcoat CA and then dyed with a dye solution • Co-deposited dye A dye is stirred into Garcoat CA and co-deposited with the lacquer • Pigmet dye The lacquer contains pigments that are co-deposited

We are specialists in the recycling of precious metals. Furthermore, we are able to achieve the best recovery rates because of many years of experience and expertise. Due to our qualified staff and equipment on the cutting edge of technology, we implement contracts quickly, accurately and carefully. We provide detailed and clear separating offers to proceed the recycling in close contact with clients and keep the transparent separating costs low.

RECYCLING MATERIALS IWG provides the opportunity to recycle all kinds of precious metals. • Used galvanic baths • Metal stripper • Anode material • Jewellery scraps • PCB

PROCESS - SAMPLE DRAW / ANALYSIS First a sample is taken from the recycling material. The samples are examined by the most modern methods of analysis, which are: • ICP • X-ray fluorescence analysis • gravimetry The customer receives the analytical result and then decides whether the material is reycled. We also offer customized solutions for billing and purchase / sale of recovered metals.

www.iwgplating.at

recycling material test results/analysis statement/account credit/transfer money sourcing new products Recycling

47

EQUIPMENT - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - EQUIPMENT

EQUIPMENT IWG also supplies equipment for electroplating. All of our equipment is designed for an easy installation, operation and maintenance.

BRUSH PLATING EQUIPMENT Simple and easy to use pen plating systems made of high quality materials. Resistant to strong acids especially designed for rhodium penplating.

ANODES IWG offers a broad range of anodes. • platinized titanium anodes • mixed oxide anodes • various metal anodes in different shapes

IWG offers all parts of pen plating equipment: • pen • different kinds of tips

RECTIFIERS FILTER SYSTEM IWG delivers filter systems for electroplating bathes. • filter pump • polypropylene cartridges • activated carbon cartridges

IWG offers rectifiers special designed for precious metal plating. • available in various power outputs • very low ripple • preadjustable

IWG offers a broad range of supplies for electroplating. Here is an excerpt of our range: small plating units, chain plating machine, brush plating equipment, rectifier, platinized titanium expanded metal and mixed oxides anodes, filter pumps, immersion heaters, precious metal reclaimer, recovery cell

www.iwgplating.at

49

QUALITY ASSURENCE AND LAB - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - QUALITY ASSURENCE AND LAB

QUALITY ASSURANCE AND LAB IWG has the necessary laboratory facilities to assure that the products are of highest quality. Each batch of our products is carefully checked to ensure that the specifications are fulfilled. Some of the state-of-the-art technology and procedures our employees utilize include: • ICP analysis for concentration estimation and identification of metals • UV/VIS analysis for concentration estimation and identification of organic compounds • CG analysis for estimation and identification of highly volatile compounds • X-ray analysis for thickness measurement • Scanning electron microscopy (SEM) for surface and thickness analysis • Auto titration equipment

The outstanding extremely high-skilled staff and the state-ofthe-art equipment of the analytical laboratories enable us to ensure very fast and accurate analysis results. IWG was always interested in the development of new processes for the electroplating business for almost 50 years. Since then tasks, equipment and procedures have been constantly adapted to the requirements of today.

www.iwgplating.at

51

IMPRINT - OUR KNOW-HOW IS YOUR SUCCESS

COLOUR RANGE - OUR KNOW-HOW IS YOUR SUCCESS

OUR KNOW-HOW IS YOUR SUCCESS - COLOUR RANGE

Colour Range Electrolytic Plating

Rhodium white C2

Rhodium black

Rhodium blue

Rhodalloy

Palladium Gapal FS

Palladium Gapal HT

Palladium Gapal TS

Palladium 174 C2

Palladium Gapal Co

Platinumbath

Ruthenium Rugadec HS2

Ruthenium Rugadec HS2/O

Ruthenium Rugadec N

Gold MC 210 H

Gold MC 211 Ti

Gold Auroprint

Gold MC 2N18

Gold MC 1N14

Gold MC 218

Gold Auroprint DE

Gold Auroprint 218 M

Gold MC 1114 S

Gold MC 1114 M

Gold MC 210 GR

Gold MC 2001

Gold MC 9000

Gold MC 9005

Gold MC 9020

Gold MC 118 GD

Gold MC 118 PI

Gold MC 3000 Argor

Gold MC 3010 Argor

Gold MC 3020 Argor

Gold MC 3030 Argor

Silver Arga 380

Whitebronze CT 15 LF

Whitebronze CT 16 LF

Yellowbronze CT 40 LF

IMPRINT: IWG PLATING Ing. W. Garhöfer Ges.m.b.H Tel. +43-(0)1-774 69 00 Fax. +43-(0)1-774 69 00-78 E-Mail: [email protected] www.iwgplating.at

IWG International - OUR KNOW-HOW IS YOUR SUCCESS

COLOUR RANGE - OUR KNOW-HOW IS YOUR SUCCESS

Colour Range Pen Plating

Gold Yellow 0N for pen plating

Gold yellow 1N for pen plating

Gold yellow 2N for pen plating

Gold yellow for pen plating

Gold Rose 1 for pen plating

Gold 5N red for pen plating

Rhodium white 5B for pen plating

Rhodium white 5E for pen plating

Rhodium white 5F for pen plating

Rhodium white 5G for pen plating

Rhodium black 3 for pen plating

Silver white for pen plating

Rhodium blue for pen plating

Palladium white for pen plating

Ruthenium natural for pen plating

Ruthenium black for pen plating

IWG HONG KONG Technology LTD. Tel. ++852-(0)-24 246 988 Fax. ++852-(0)-24 239 733 [email protected] www.iwg-plating.com.hk

IWG THAILAND CO. LTD. Tel. ++662-(0)-921 58 85-7 Fax. ++662-(0)-921 58 84 [email protected] www.iwgplating.at

IWG TURKEY Ayba Celik Ic Ve Dis Ticaret Tel. ++90-212-603 19 73 Fax. ++90-212-603 19 74 [email protected] www.aybacelik.com

IWG RUSSIA / UKRAINE Ayba Celik Ic Ve Dis Ticaret Tel. (RU) ++7 915 903 4952 Tel. (UA) ++380 67 999 7694 [email protected] www.aybacelik.com

IWG SYRIA / LEBANON Jaghlasian Trading Tel. (SY) ++963-21-444 42 13-46 59 616 Tel: (LB) ++961-1-48 75 18-9 [email protected] www.jaghlasian.com

IWG INDIA MUMBAI M. Sakshi international Tel: ++91-22-23 41 01 79 Fax: ++91-22-40 05 16 77 [email protected]

IWG IRAN Sama Chimie Saz Trading Co Tel. ++98-21-885 18 553-4 Fax. ++98-21-885 29 858 [email protected] www.samachimie.com

IWG UNITED ARAB EMIRATES Sama Chimie Saz International Trading Tel. ++971-6-5576052 & 04 266 1208 Fax. ++971-6-5576053 & 04 266 1408 [email protected]

IWG INDIA JAIPUR Arihant Sai Traders Tel: ++91-141-27 92 261 Fax: ++91-141-27 92 280